德国拜耳/泰国拜耳/上海拜耳PC/ABS T88 GF20 原厂原包,货真价实,价格优惠,亲!~
专业供应PC+ABS塑胶原料:防火PC+ABS,阻燃PC+ABS,耐高温PC+ABS,耐热PC+ABS,抗冲击PC+ABS,食品级PC+ABS,高冲击PC+ABS,抗紫外线PC+ABS,低粘度PC+ABS,电镀级PC+ABS,加玻纤PC+ABS,耐低温PC+ABS,高流动PC+ABS,无卤PC+ABS,无溴PC+ABS,注塑级PC+ABS,等塑胶原料。
德国拜耳/泰国拜耳/上海拜耳PC/ABS T88 GF20物性表
Physical |
Nominal Value
|
Unit
|
Test Method
|
Density
|
1290
|
kg/m³
|
ISO 1183 2 |
Molding Shrinkage - Flow
|
0.20 to 0.40
|
%
|
ISO 2577 2 |
Molding Shrinkage - Across Flow
|
0.30 to 0.50
|
%
|
ISO 2577 2 |
Water Absorption (Saturation)
|
0.40
|
%
|
ISO 62 2 |
Water Absorption (Equilibrium)
|
0.20
|
%
|
ISO 62 2 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile modulus
|
7200
|
MPa
|
ISO 527-2 2 |
Tensile Stress (Yield, 23°C)
|
120
|
MPa
|
ISO 527-2/5 |
Tensile Stress (Break)
|
120
|
MPa
|
ISO 527-2 2 |
Tensile Strain (Yield, 23°C)
|
2.4
|
%
|
ISO 527-2/5 |
Tensile Strain (Break)
|
2.4
|
%
|
ISO 527-2 2 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Notched Izod Impact Strength
|
ISO 180/A | ||
-30°C
|
8.0
|
kJ/m²
|
|
23°C
|
8.0
|
kJ/m²
|
|
Unnotched Izod Impact Strength
|
ISO 180 | ||
-30°C
|
38
|
kJ/m²
|
|
23°C
|
38
|
kJ/m²
|
|
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Deflection Temperature Under Load (0.45 MPa)
|
129
|
°C
|
ISO 75-2 2 |
Deflection Temperature Under Load (1.8 MPa)
|
119
|
°C
|
ISO 75-2 2 |
Vicat Softening Temperature
|
130
|
°C
|
ISO 306/B120 |
Vicat Softening Temperature (50°C/h, B (50N))
|
128
|
°C
|
ISO 306 2 |
CLTE - Flow
|
0.000030
|
cm/cm/°C
|
ISO 11359-2 2 |
CLTE - Transverse
|
0.000065
|
cm/cm/°C
|
ISO 11359-2 2 |
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Surface resistivity
|
1.0E+17
|
ohm
|
IEC 60093 2 |
Volume resistivity
|
1.0E+14
|
ohm·m
|
IEC 60093 2 |
Electric strength
|
35
|
kV/mm
|
IEC 60243-1 2 |
Relative Permittivity (100 Hz)
|
3.30
|
|
IEC 60250 2 |
Relative Permittivity (1 MHz)
|
3.20
|
|
IEC 60250 2 |
Dissipation Factor (100 Hz)
|
0.0025
|
|
IEC 60250 2 |
Dissipation Factor (1 MHz)
|
0.0085
|
|
IEC 60250 2 |
Comparative tracking index
|
150
|
|
IEC 60112 2 |
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Flame Rating (0.850 mm)
|
HB
|
|
UL 94 |
Fill Analysis |
Nominal Value
|
Unit
|
Test Method
|
Melt Viscosity (260°C, 1000 sec^-1)
|
205
|
Pa·s
|
ISO 11443-A |
Additional Information |
Nominal Value
|
Unit
|
Test Method
|
Glass Fiber Content 3
|
20
|
%
|
ISO 3451-1 |