| * 厂家（产地）： | 台湾奇美 | * 牌号： | PC-365 |
| * 销售方式： | 品牌经销 | 备注说明： | 原厂原包，货到付款 |
| * 地区： | 全国 |
台湾奇美PC/ABS,PC-365原厂原包，台湾奇美PC/ABS,PC-365货真价实，台湾奇美PC/ABS,PC-365价格优惠，亲！~
专业供应PC+ABS塑胶原料：防火PC+ABS,阻燃PC+ABS，耐高温PC+ABS，耐热PC+ABS，抗冲击PC+ABS，食品级
PC+ABS，高冲击PC+ABS，抗紫外线PC+ABS，低粘度PC+ABS，电镀级PC+ABS，加玻纤PC+ABS，耐低温PC+ABS
，高流动PC+ABS，无卤PC+ABS，无溴PC+ABS，注塑级PC+ABS，等塑胶原料。
台湾奇美PC/ABS,PC-365英文物性表
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.13
|
g/cm³
|
ASTM D792 |
|
Density
|
1.13
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg)
|
20
|
g/10 min
|
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR) (260°C/3.8 kg)
|
13.0
|
cm³/10min
|
ISO 1133 |
|
Molding Shrinkage - Flow
|
0.40 to 0.60
|
%
|
ASTM D955 |
|
Water Absorption (23°C, 24 hr)
|
0.40
|
%
|
ASTM D570 |
|
Spiral Flow Length 2 (260°C)
|
9.80
|
cm
|
Internal Method |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength (Yield, 23°C)
|
53.0
|
MPa
|
ASTM D638 |
|
Tensile Stress (Yield)
|
50.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Stress (Break)
|
46.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Elongation (Break, 23°C)
|
85
|
%
|
ASTM D638 |
|
Tensile Strain (Break)
|
80
|
%
|
ISO 527-2/50 |
|
Flexural Modulus (23°C)
|
2260
|
MPa
|
ASTM D790 |
|
Flexural Modulus 3
|
2300
|
MPa
|
ISO 178 |
|
Flexural Strength (23°C)
|
78.5
|
MPa
|
ASTM D790 |
|
Flexural Strength 3
|
80.0
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (3.18 mm)
|
540
|
J/m
|
ASTM D256 |
|
Notched Izod Impact Strength
|
45
|
kJ/m²
|
ISO 180/1A |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
110
|
|
ASTM D785 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
106
|
°C
|
ASTM D648 |
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
106
|
°C
|
ISO 75-2/A |
|
Heat Deflection Temperature (1.8 MPa, Annealed)
|
117
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
136
|
°C
|
ASTM D1525 4 |
|
Vicat Softening Temperature
|
|||
|
--
|
136
|
°C
|
ISO 306/A50 |
|
--
|
123
|
°C
|
ISO 306/B50 |
|
CLTE - Flow (40 to 100°C)
|
0.000060 to 0.000080
|
cm/cm/°C
|
ASTM D696 |
|
RTI Elec
|
UL 746 | ||
|
1.50 mm
|
60.0
|
°C
|
|
|
3.00 mm
|
60.0
|
°C
|
|
|
RTI Imp
|
UL 746 | ||
|
1.50 mm
|
60.0
|
°C
|
|
|
3.00 mm
|
60.0
|
°C
|
|
|
RTI Str
|
UL 746 | ||
|
1.50 mm
|
60.0
|
°C
|
|
|
3.00 mm
|
60.0
|
°C
|
|
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Arc Resistance
|
PLC 7
|
|
ASTM D495 |
|
Comparative Tracking Index (CTI)
|
PLC 2
|
|
UL 746 |
|
High Amp Arc Ignition (HAI)
|
UL 746 | ||
|
1.50 mm
|
PLC 0
|
|
|
|
3.00 mm
|
PLC 0
|
|
|
|
High Voltage Arc Tracking Rate (HVTR)
|
PLC 2
|
|
UL 746 |
|
Hot-wire Ignition (HWI)
|
UL 746 | ||
|
1.50 mm
|
PLC 4
|
|
|
|
3.00 mm
|
PLC 4
|
|
|
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
1.50 mm, ALL
|
HB
|
|
|
|
3.00 mm, ALL
|
HB
|
|
|
|
Flammability Classification
|
IEC 60695-11-10, -20 | ||
|
3.00 mm
|
HB40
|
|
|
|
1.50 mm
|
HB75
|
|
关于我们 | 广告服务 | 网站地图 | 法律声明 | 联系我们 | 免责声明 | 人才招聘 | 友情链接
Copyright©2010-2024 ccedip.com. All Rights Reserved
粤ICP备06018398号-13 
粤公网安备44030402000782号
手机版塑胶网
官方微信
手机版APP（安卓）