| * 厂家（产地）： | 美国杜邦 | * 牌号： | 151L NC010 |
| * 销售方式： | 品牌经销 | 备注说明： | 原厂正牌，货到付款 |
| * 地区： | 全国 |
美国杜邦PA66 151L 原厂原包，货真价实，价格优惠，亲！~
本公司长期供应透明尼龙，改性尼龙，食品级尼龙，阻燃尼龙，防火（UL94V0、5VA级）尼龙，耐磨尼龙，超韧性尼龙，耐寒耐低温尼龙，耐酸碱尼龙，抗紫外线尼龙，防水解尼龙，抗水解尼龙，增强尼龙，不吸水尼龙，无卤尼龙，热稳定尼龙，弹性尼龙，硬尼龙，挤出尼龙，注塑尼龙，等塑胶原料。
美国杜邦PA66 151L物性表
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Specific Gravity |
1.06
|
--
|
g/cm³
|
ASTM D792 |
| Density |
1.06
|
--
|
g/cm³
|
ISO 1183 |
| Molding Shrinkage - Flow (3.20 mm) |
1.1
|
--
|
%
|
Internal Method |
| Molding Shrinkage - Across Flow (3.20 mm) |
1.1
|
--
|
%
|
Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
|
Across Flow: 2.00 mm
|
1.4
|
--
|
%
|
|
|
Flow: 2.00 mm
|
1.3
|
--
|
%
|
|
| Water Absorption (23°C, 24 hr) |
0.25
|
--
|
%
|
ASTM D570 |
| Water Absorption (Saturation, 23°C) |
3.0
|
--
|
%
|
ASTM D570 |
| Water Absorption (Saturation, 23°C) |
3.0
|
--
|
%
|
ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) |
1.3
|
--
|
%
|
ISO 62 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Tensile Modulus (23°C) |
2400
|
1700
|
MPa
|
ISO 527-2 |
| Tensile Strength | ASTM D638 | |||
|
-40°C
|
94.0
|
93.0
|
MPa
|
|
|
23°C
|
61.0
|
52.0
|
MPa
|
|
|
77°C
|
41.0
|
36.0
|
MPa
|
|
| Tensile Strength | ASTM D638 | |||
|
Yield, -40°C
|
94.0
|
93.0
|
MPa
|
|
|
Yield, 23°C
|
61.0
|
51.0
|
MPa
|
|
|
Yield, 77°C
|
30.0
|
35.0
|
MPa
|
|
| Tensile Stress (Yield, 23°C) |
62.0
|
54.0
|
MPa
|
ISO 527-2 |
| Tensile Elongation | ASTM D638 | |||
|
Yield, -40°C
|
8.0
|
10
|
%
|
|
|
Yield, 23°C
|
7.0
|
30
|
%
|
|
|
Yield, 77°C
|
30
|
40
|
%
|
|
| Tensile Strain (Yield, 23°C) |
4.5
|
18
|
%
|
ISO 527-2 |
| Tensile Elongation | ASTM D638 | |||
|
Break, -40°C
|
10
|
20
|
%
|
|
|
Break, 23°C
|
100
|
250
|
%
|
|
|
Break, 77°C
|
230
|
> 300
|
%
|
|
| Nominal Tensile Strain at Break (23°C) |
17
|
> 50
|
%
|
ISO 527-2 |
| Flexural Modulus | ASTM D790 | |||
|
-40°C
|
2340
|
2760
|
MPa
|
|
|
23°C
|
2030
|
1240
|
MPa
|
|
|
77°C
|
410
|
380
|
MPa
|
|
| Flexural Modulus (23°C) |
2100
|
1440
|
MPa
|
ISO 178 |
| Shear Strength (23°C) |
58.0
|
--
|
MPa
|
ASTM D732 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
|
-30°C
|
3.5
|
3.0
|
kJ/m²
|
|
|
23°C
|
3.5
|
4.0
|
kJ/m²
|
|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
|
-30°C
|
No Break
|
40 kJ/m²
|
|
|
|
23°C
|
No Break
|
No Break
|
|
|
| Notched Izod Impact | ASTM D256 | |||
|
-40°C
|
32
|
21
|
J/m
|
|
|
23°C
|
43
|
69
|
J/m
|
|
| Notched Izod Impact Strength | ISO 180/1A | |||
|
-30°C
|
4.5
|
3.0
|
kJ/m²
|
|
|
23°C
|
4.0
|
4.5
|
kJ/m²
|
|
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Rockwell Hardness (R-Scale) |
114
|
103
|
|
ASTM D785 |
| Rockwell Hardness (R-Scale) |
114
|
--
|
|
ISO 2039-2 |
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Heat Deflection Temperature (0.45 MPa, Unannealed) |
135
|
--
|
°C
|
ISO 75-2/B |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) |
55.0
|
--
|
°C
|
ASTM D648 |
| Heat Deflection Temperature (1.8 MPa, Unannealed) |
62.0
|
--
|
°C
|
ISO 75-2/A |
| Brittleness Temperature |
-120
|
-107
|
°C
|
ASTM D746 |
| Melting Temperature |
218
|
--
|
°C
|
ASTM D3418 |
| Melting Temperature 2 |
218
|
--
|
°C
|
ISO 11357-3 |
| CLTE - Flow | ISO 11359-2 | |||
|
-40 to 23°C
|
0.000090
|
--
|
cm/cm/°C
|
|
|
23 to 55°C
|
0.00011
|
--
|
cm/cm/°C
|
|
|
55 to 160°C
|
0.00016
|
--
|
cm/cm/°C
|
|
| CLTE - Transverse | ISO 11359-2 | |||
|
-40 to 23°C
|
0.000090
|
--
|
cm/cm/°C
|
|
|
23 to 55°C
|
0.00012
|
--
|
cm/cm/°C
|
|
|
55 to 160°C
|
0.00018
|
--
|
cm/cm/°C
|
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Surface Resistivity |
1.0E+12
|
--
|
ohms
|
IEC 60093 |
| Volume Resistivity (23°C) |
1.0E+15
|
1.0E+16
|
ohm·cm
|
ASTM D257 |
| Volume Resistivity |
1.0E+15
|
1.0E+13
|
ohm·cm
|
IEC 60093 |
| Dielectric Strength 3 | ASTM D149 | |||
|
23°C, 3.20 mm
|
14
|
--
|
kV/mm
|
|
|
93°C
|
7.1
|
--
|
kV/mm
|
|
| Relative Permittivity | IEC 60250 | |||
|
23°C, 100 Hz
|
3.60
|
5.10
|
|
|
|
23°C, 1 MHz
|
3.20
|
4.00
|
|
|
| Dissipation Factor | ASTM D150 | |||
|
23°C, 100 Hz
|
0.020
|
0.15
|
|
|
|
23°C, 1 kHz
|
0.020
|
0.15
|
|
|
|
23°C, 1 MHz
|
0.020
|
0.10
|
|
|
| Dissipation Factor | IEC 60250 | |||
|
23°C, 100 Hz
|
0.014
|
0.070
|
|
|
|
23°C, 1 MHz
|
0.016
|
0.040
|
|
|
| Comparative Tracking Index |
> 600
|
--
|
V
|
ASTM D3638 |
| Comparative Tracking Index |
600
|
--
|
V
|
IEC 60112 |
| Electric Strength (23°C, 2.00 mm) |
22
|
21
|
kV/mm
|
IEC 60243-1 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Flame Rating - UL | UL 94 | |||
|
0.860 mm
|
V-2
|
--
|
|
|
|
1.50 mm
|
V-2
|
--
|
|
|
|
3.00 mm
|
V-2
|
--
|
|
|
| Flammability Classification | IEC 60695-11-10, -20 | |||
|
0.860 mm
|
V-2
|
--
|
|
|
|
1.50 mm
|
V-2
|
--
|
|
|
|
3.00 mm
|
V-2
|
--
|
|
|
| Oxygen Index |
27
|
--
|
%
|
ISO 4589-2 |
| UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| RTI Str | UL 746 | |||
|
0.860 mm
|
65.0
|
--
|
°C
|
|
|
1.47 mm
|
65.0
|
--
|
°C
|
|
|
3.00 mm
|
65.0
|
--
|
°C
|
|
| RTI Imp | UL 746 | |||
|
0.860 mm
|
65.0
|
--
|
°C
|
|
|
1.47 mm
|
65.0
|
--
|
°C
|
|
|
3.00 mm
|
65.0
|
--
|
°C
|
|
| RTI Elec | UL 746 | |||
|
0.860 mm
|
105
|
--
|
°C
|
|
|
1.47 mm
|
105
|
--
|
°C
|
|
|
3.00 mm
|
105
|
--
|
°C
|
|
| Comparative Tracking Index (CTI) |
> 600
|
--
|
V
|
UL 746 |