| * 厂家（产地）： | 美国杜邦 | * 牌号： | 408HS NC010/BK009 |
| * 销售方式： | 品牌经销 | 备注说明： | 原厂正牌，货到付款 |
| * 地区： | 全国 |
本公司长期供应透明尼龙，改性尼龙，食品级尼龙，阻燃尼龙，防火（UL94V0、5VA级）尼龙，耐磨尼龙，超韧性尼龙，耐寒耐低温尼龙，耐酸碱尼龙，抗紫外线尼龙，防水解尼龙，抗水解尼龙，增强尼龙，不吸水尼龙，无卤尼龙，热稳定尼龙，弹性尼龙，硬尼龙，挤出尼龙，注塑尼龙，等塑胶原料。
美国杜邦PA66 408HS NC010/BK009物性表
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Density |
1.10
|
--
|
g/cm³
|
ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
|
Across Flow: 2.00 mm
|
1.6
|
--
|
%
|
|
|
Flow: 2.00 mm
|
1.6
|
--
|
%
|
|
|
Flow: 3.20 mm
|
1.5
|
--
|
%
|
|
| Water Absorption (Saturation, 23°C) |
7.0
|
--
|
%
|
ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) |
2.0
|
--
|
%
|
ISO 62 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Tensile Modulus (23°C, 4.00 mm) |
2300
|
985
|
MPa
|
ISO 527-2 |
| Tensile Stress (Yield, 23°C, 4.00 mm) |
63.0
|
43.0
|
MPa
|
ISO 527-2 |
| Tensile Strain (Yield, 23°C, 4.00 mm) |
5.0
|
29
|
%
|
ISO 527-2 |
| Nominal Tensile Strain at Break (23°C, 4.00 mm) |
37
|
> 50
|
%
|
ISO 527-2 |
| Poisson's Ratio |
0.42
|
--
|
|
|
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
|
-30°C
|
18
|
11
|
kJ/m²
|
|
|
23°C
|
19
|
26
|
kJ/m²
|
|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
|
-30°C
|
No Break
|
420 kJ/m²
|
|
|
|
23°C
|
No Break
|
No Break
|
|
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Heat Deflection Temperature (0.45 MPa, Unannealed) |
176
|
--
|
°C
|
ISO 75-2/Bf |
| Heat Deflection Temperature (1.8 MPa, Unannealed) |
63.0
|
--
|
°C
|
ISO 75-2/Af |
| Melting Temperature 2 |
263
|
--
|
°C
|
ISO 11357-3 |
| CLTE - Flow (23 to 55°C) |
0.00011
|
--
|
cm/cm/°C
|
ISO 11359-2 |
| CLTE - Transverse (23 to 55°C) |
0.00013
|
--
|
cm/cm/°C
|
ISO 11359-2 |
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Surface Resistivity (2.00 mm) |
1.0E+12
|
--
|
ohms
|
IEC 60093 |
| Volume Resistivity (2.00 mm) |
1.0E+14
|
--
|
ohm·cm
|
IEC 60093 |
| Relative Permittivity | IEC 60250 | |||
|
23°C, 2.00 mm, 100 Hz
|
3.50
|
--
|
|
|
|
23°C, 2.00 mm, 1 MHz
|
3.30
|
--
|
|
|
| Dissipation Factor | IEC 60250 | |||
|
100 Hz
|
0.0075
|
--
|
|
|
|
1 MHz
|
0.013
|
--
|
|
|
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Flame Rating - UL | UL 94 | |||
|
0.810 mm
|
HB
|
--
|
|
|
|
1.50 mm
|
HB
|
--
|
|
|
|
3.00 mm
|
HB
|
--
|
|
|
| Flammability Classification | IEC 60695-11-10, -20 | |||
|
0.810 mm
|
HB
|
--
|
|
|
|
1.50 mm
|
HB
|
--
|
|
|
|
3.00 mm
|
HB
|
--
|
|
|
| Oxygen Index |
22
|
--
|
%
|
ISO 4589-2 |
| UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| RTI Str | UL 746 | |||
|
0.810 mm
|
85.0
|
--
|
°C
|
|
|
1.50 mm
|
85.0
|
--
|
°C
|
|
|
3.00 mm
|
85.0
|
--
|
°C
|
|
| RTI Imp | UL 746 | |||
|
0.810 mm
|
75.0
|
--
|
°C
|
|
|
1.50 mm
|
75.0
|
--
|
°C
|
|
|
3.00 mm
|
75.0
|
--
|
°C
|
|
| RTI Elec | UL 746 | |||
|
0.810 mm
|
125
|
--
|
°C
|
|
|
1.50 mm
|
125
|
--
|
°C
|
|
|
3.00 mm
|
125
|
--
|
°C
|
|
| Comparative Tracking Index (CTI) (3.00 mm) |
> 600
|
--
|
V
|
UL 746 |
| Hot-wire Ignition (HWI) | UL 746 | |||
|
0.810 mm
|
9.0
|
--
|
sec
|
|
|
1.50 mm
|
11
|
--
|
sec
|
|
|
3.00 mm
|
25
|
--
|
sec
|
|
| High Amp Arc Ignition (HAI) | UL 746 | |||
|
0.810 mm
|
200
|
--
|
|
|
|
1.50 mm
|
180
|
--
|
|
|
|
3.00 mm
|
200
|
--
|
|
关于我们 | 广告服务 | 网站地图 | 法律声明 | 联系我们 | 免责声明 | 人才招聘 | 友情链接
Copyright©2010-2024 ccedip.com. All Rights Reserved
粤ICP备06018398号-13 
粤公网安备44030402000782号
手机版塑胶网
官方微信
手机版APP（安卓）